Vortex control in slurry molding applications

ABSTRACT

A molding head is especially adapted for vacuum molding or forming of structures and, in particular, fibrous composite structures in an adjustable, controllable three dimensional orientation before, during and after molding. Such a molding head includes a mold plate with narrow slots in the mold surface thereof and wider channels in the back surface thereof, with such slots and channels intersecting one another. A control system of servomotors or other actuators permits movement and orientation of the mold head during forming, thereby creating the ability to vary the material properties based on gravity and particle or suspension grain, thickness and other now controllable properties.

CROSS REFERENCES TO RELATED APPLICATIONS

This application is a divisional application of pending U.S. patentapplication Ser. No. 11/592,660 filed Nov. 3, 2006 which is acontinuation in part of pending U.S. patent application Ser. No.11/106,096 filed Apr. 14, 2005 which, in turn, claims priority under 35U.S.C. 109(e) from expired U.S. Provisional Patent application Ser. No.60/562,015 filed Apr. 14, 2004, all of which are incorporated herein byreference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates generally to a process for molding orforming items from pulp, slurries, or other suspensions and productsobtained thereby. The vacuum mold head or mold plate in the apparatus isgiven the ability to be located in various orientations within thematerial holding tank, thereby creating the ability to control thevortex created during the molding process. By controlling the vortex thematerial properties can be controlled, particularly, when utilizingslurries with low solids concentrations.

2. Related Art

The forming process of items, particularly those formed from solutionsof pulps, slurries or suspensions have, up to now, never had a way tocontrol the direction of gravity during the forming process. In theprior art, once the mold was set up, the direction of gravity was fixedrelative to the mold. Gravity effects on the suspended particles in thesuspensions would, during the forming process, sometimes causenon-uniform surface effects in the formed piece. What is needed in theart is a mechanism to control the orientation of the vacuum mold headrelative to gravity.

The use of a vacuum mold head is well known in the art. In co-pendingU.S. patent application Ser. No. 11/106,096 a device with anarticulating, or gambrel, arm is described along with the ability tocontrol the orientation of the vacuum mold head relative to gravity.This advance in the mechanism has led to further understanding in thedynamics of fiber deposition and allowed further advances in theproperties which can be obtained.

Through diligent research it has now been realized that fibers can beselectively oriented by controlling the motion of the vacuum mold headto increase the physical strength of the final product.

Vacuum forming techniques are characterized by the use of a mold headwhich has a vacuum, or suction, applied to one side of the mold head.The mold head is lowered into a slurry of fibers. As the slurry is drawnthrough the mold head the fibers deposit thereby forming the preform bydepletion of the solids in the slurry. The solvent, typically with someconcentration of fibers, passes through the filter and is eitherdiscarded or recycled. It is widely known that the slurry tends to forma vortex due to the act of drawing the slurry through a void. In extremecases when the fiber, or solids content is very low, the vortex isapproximately centrally located over the vacuum port. In many cases theimpact of the vortex can be measured as variations in thickness from thecenter of the vortex outward. There have been many attempts to alleviatethis problem by techniques such as varying the sizes of the voids, usingbaffles in the slurry, introducing air flow into the slurry to disruptthe local flow and other techniques. These techniques are insufficientand difficult to set up. Baffles, for example, are widely used. Thelocation of the baffles is typically done by trial and error whichrequires a substantial amount of effort. If the product is changed thebaffling must also be changed in ways which are not easily predicted.This leads to wasted time and effort and makes it difficult to quicklychange from one product to another. Furthermore, the baffles aretypically fixed relative to the tank, and within the solution, whichlimits changes during the fiber deposition process.

Even with the best efforts current techniques are not sufficient andtend to be counterproductive by slowing the formation process. Dependingon the shape and design of the mold head the vortex formation can belocalized with a vortex for each void or it can be larger with a vortexcovering larger areas of the filter. The vortex causes fibers tocongregate and at least partially align approximately tangentially tothe vortex within the slurry. This tangential alignment of fiber orsolids may be used to increase the preform thickness in desired areaswithout baffling which tends to slow the formation process. As thefibers reach the filter there is, at least, localized fiber orientationor alignment. As would be realized fibers which are parallel andoverlaid do not form a strong matrix and must be cross-linked, or cured,to represent a rigid structure.

Through diligent research the present inventor has developed a processfor slurry molding applications which can disrupt localized fiberalignment with minimal efforts and without reliance on baffles or flowcontrol techniques. Furthermore, the disruption provides a producthypothesized to have fibers oriented in a manner which approachesrandomness and which are interlaced resulting in significant increasesin strength relative to conventionally formed slurry molded products.

SUMMARY OF THE INVENTION

The present invention includes a molding head process especially adaptedfor vacuum molding or forming of structures and, in particular, fibrousor particulate composite structures wherein the fibers are randomlyoriented thereby providing a stronger matrix.

Yet another advantage of the present invention is that the invention canbe used in conjunction with a pulp molding/die-dried process. One suchprocedure can be felting or molding a blank from a fibrous suspensionusing the mold head.

An advantage stemming from the ability to manipulate fiber or moldedpart orientation is that a multi-layer component can be developed inwhich fibers are oriented in each layer so as to promote drainagetherethrough and/or to achieve a desired set of product characteristics.

Yet another advantage of the present invention is the ability to providea multi-layered composite of differing materials accurately and undersufficient control to quickly and economically provide novel structuresor conventional structures with improved properties.

Yet another advantage of the present invention is that a wide range ofcomposite/homogeneous structures can be formed of any of various sizes,shapes, and/or compositions.

These and other advantages, as will be realized, are provided in amolding system. The molding system has a container for holding materialto be molded. A mold head is provided on which material is be molded. Atleast one arm is attached to the mold head and capable of moving themold head in three-dimensions within the container.

Yet another embodiment is provided in a process for forming a moldedpart. The process includes providing a container for holding a materialto be molded. The molding head is placed into the material wherein themolding head has passages there through. A reduced pressure is appliedto the molding head to draw material through the passages. The moldinghead is moved in three dimensions within the material and a molded partis formed on the molding head.

Yet another embodiment is provided in a molded part formed by theprocess of: providing a container for holding a material to be molded;

placing a molding head into the material wherein the molding headcomprises passages there through;applying a reduced pressure to the molding head to draw material throughthe passages; moving the molded part in three dimensions within thematerial; andforming the molded part on the molding head.

Yet another embodiment is provided in a process for forming a moldedpart. The process includes providing a container for holding a materialto be molded. The mold head is preferably equipped with vortexgenerators, or fences, to expand or intensify the vortex spin and may bemounted above or below the mold screen media. The molding head is placedinto the material wherein the molding head has passages there through. Areduced pressure is applied to the molding head to draw material throughthe passages, vortex generators and/or fences. By combining thegenerated vortex's and the three dimensional movement of the mold headas the material is drawn onto, or repelled from, the mold screen mediaused on the mold head to form a part.

BRIEF DESCRIPTION OF THE DRAWINGS

The features and advantages of this invention, and the manner ofattaining them, will become more apparent and the invention will bebetter understood by reference to the following descriptions of theembodiments of the invention taken in conjunction with the accompanyingdrawings.

FIG. 1 is an diagrammatic perspective view of the molding system of oneembodiment the present invention.

FIG. 2 is a diagrammatic perspective, partially cut-away view of themold head of FIG. 1, shown in an alternate orientation.

FIG. 3 is a diagrammatic perspective view of an alternate embodiment ofthe molding system for producing various size and shape molded articlesshowing an alternate system of controlling the three dimensionalorientation of the mold head.

FIG. 4 is a diagrammatic representation of an advantage of the presentinvention.

FIG. 5 is a schematic diagram of a device for formation of multi-layeredproducts.

FIG. 6 is a schematic illustration of an embodiment of the presentinvention.

FIGS. 7 and 8 are schematic representations of the mechanism of thepresent invention.

The exemplifications set out herein illustrate at least one preferredembodiment of the invention, in one form, and such exemplifications arenot to be construed as limiting the scope of the invention in anymanner.

DETAILED DESCRIPTION OF THE INVENTION

A molding system 10 of the present invention is illustrated in FIGS. 1,2 and 3. The molding system, 10, includes a mold head 4 (FIG. 1-2) or 14(FIG. 3). Molding heads can be manufactured from materials common in theart including, but not limited to, steel, aluminum, brass, stainlesssteel and composites.

Mold head 4, 14 is located in three dimensional space by at least onearm 5 (FIG. 1-2) comprised of linear servos or other manually orcomputer controllable actuating systems, that can fix and or relocatethe three dimensional position of mold head 4, 14 during molding withina tank 1 of slurry, pulp, or other suspension. Tank 1 is supplied withan agitation system 2 to continuously and substantially completelymaintain the homogeneity of the pulp, slurry or suspension within tank 1used as the constituent material for the molded article to be formed onhead 4, 14. In one embodiment the agitation system comprises a rotatablenozzle, 3, which recirculates solution within the tank by a pressurizedflow. The agitation system can be a rotatable nozzle, a mixer blade oran air bubbler. Rotatable nozzles and mixer blades are preferable foreasily suspended materials and an air bubbler is preferred for materialsthat are difficult to suspend in a slurry.

The mold head preferably has vacuum or suction ports for providing areduced pressure thereby drawing the molding liquid through the moldhead while depositing suspended fibers on the mold head. The vacuumports may have channels or slots and may be arranged co-parallel ornearly so to each other to promote uniform fluid flow through the moldface. Yet it may prove advantageous to arrange the slots in any of avariety of patterns, for example: a star-shape, a series of concentriccircles, a spiral-shape, a series of nested polygons, or potentially anon-regular pattern. The collection of vacuum ports is also referred toas a mold screen. Any of these or other patterns may be chosen toachieve a desired fluid flow for mold head 4, 14. While in mostinstances a uniform fluid flow will be desired, there may be instancesin which a controlled non-uniformed fluid flow is desired to therebyspecifically create variances in the surface of the part, or preform,being formed. No matter the pattern, it is generally preferable thatslots be made as narrow as possible yet still able to sufficiently ventsteam and/or drain the fluid (i.e., liquid or gas) portion of themolding suspension there through.

The molding system 10 is advantageously used as part of a moldingarrangement system which further incorporates a vacuum device (8, FIG.3). Vacuum device 8, as illustrated in FIG. 3, is connected to and mayinclude a vacuum mold head 14, and a plurality of vacuum conduits 11,interconnected for relative articulation by rotary unions 7, allowingmovement with three degrees of freedom of mold head 14 relative togravity. Located at each rotary union 7 are servos 6 or other devices toaccurately control the positioning of the conduits 11, which wouldnecessarily then control the placement and orientation of mold head 14in three dimensional space relative to tank 1, agitator, 3, and gravity.A servo mechanism 5 connected to vacuum device, 8, permits the assemblyto be removed from the liquid or source material of tank 1 whennecessary.

It is advantageous for vacuum device, 8, to be adjustable with regardsto the internal pressure and relative position.

The embodiments of molding arrangement shown in FIGS. 1-2 illustrate thevariety of complex orientations, which may be utilized in the mold orforming process of the invention. As can be seen from FIGS. 1 and 2,mold head 4 can be developed for movement or controlled orientationwithin tank 1, thereby causing formation of thicker, shaped pieces orfor molding thin fragile parts, or in all cases controlling the settlingof movement of the material from suspension onto the mold forming head.By changing the effective length of arms 5, the head location may bechanged before, during or after molding.

FIG. 3 illustrates a system designed for locating the mold head, 14,within the tank, 1, during the forming process, preferably, whileapplying vacuum or suction through mold head, 14, causing articles insuspension to build in thickness on the surface of the mold head. In theembodiment of FIG. 3, servos 6 change relative locations between vacuumconduits 11, which therefore change the location of mold head, 14,within and relative to tank 1, the suspension therein, and mostimportantly gravity.

A particular advantage of the present invention is describedschematically with reference to FIG. 4. In FIG. 4 a mold head isillustrated at 40. Imposed on the mold head is a series of orthogonalaxis with the y-axis being perpendicular to the page and the x-axis andz-axis being coplanar and in the plane of the page. The orientation ofthe orthogonal axis system is by convention and any axis system could beused to describe the motion. For the purposes of discussion the primaryaxis system has an origin at the approximate center (C) of the mold headwhile two secondary axis systems are at arbitrary points (A) and (B).

It has long been the practice in mold forming to have an appropriatelyshaped mold which is lowered into a slurry. For the purposes of thepresent invention this corresponds to movement along the Y-axis. In someapplications, such as the manufacture of paper, the mold form iswithdrawn from the solution and then translated back-and-forth withinthe plane of the mold to allow fibers to orient in parallel fashion.

Through diligent research it has been surprisingly realized thatproviding a third degree of motion within the slurry allows the fiberdistribution to be more carefully controlled by altering the vortices inthe slurry. It has long been the approach to alter the vortex bycontrolling the flow of the slurry.

By way of explanation, again with reference to FIG. 4, the mold head,40, can be lowered into the slurry and moved in various randomdirections thereby insuring that the flow dynamics on the face of themold head vary with time during the fiber deposition process. Theability to translate the mold head in three dimensions also allows fiberbuildup to be varied. By way of explanation, if the mold head is rotatedapproximately around the center point (C) the arbitrary point (A) canmove through the slurry at a different rate than arbitrary point (B).The net effect is a fiber accumulation at arbitrary point (A) that isdifferent from that at point (B). The difference in fiber accumulationis a function of rotation rate, solids content and solution rheology. Bycomparison with the prior art this type of variation would requirebaffling to alter the fiber deposition over arbitrary point (A) relativeto the fiber deposition over arbitrary point (B). The baffling disruptsthe overall flow in the tank which is detrimental to homogeneity of theslurry. By selectively controlling the movement of the mold head thehomogeneity of the slurry can be maintained throughout the tank whilecertain regions of the mold head can be accelerated, or deceleratedthrough the slurry as desired.

It is well within the scope of the present invention to create a moldingarrangement for forming cylinders, domes, or other complex convoluted orirregular shapes, including, parts with raised portions and/orvalleys/grooves. As a result, it is possible to use the moldingarrangements system to create any of a variety of preform componentsincluding, but not limited to audio speakers, composite parts,multi-layer parts and the like. Even more particularly complex itemsformed from carbon fibers, KEVLAR® (para-aramid) fibers or other itemspulled out of suspension and formed, molded or laid-up on head 4, 14 canbe formed.

The molding procedure can, more particularly, be used with respect totwo procedures associated with pulp molding. The first procedure is thefelting of a paper/pulp blank where the mold head 4, 14 is covered witha suspension made up of wood pulp, a synthetic blend of fibers, carbonfibers, fiberglass, ceramic fibers, ceramic fiber precursors and/orother types of fibers along with water and/or another suspension fluid(e.g., another liquid or, potentially, a gas). The fibers can bestraight fibers, fibrillated fibers or flocked fibers. It is also to beunderstood that such a suspension may also include, for example,chemicals (such as dispersants) which contribute to the suspensionchemistry and/or ingredients such as binders which aid characteristicsof the formed felted blank or preform.

Upon covering the mold head 4, 14 with the desired suspension, a vacuumis applied to the mold head via vacuum device, 8, or conduits, 11, inorder to draw the water and/or other carrying medium from thesuspension, thereby resulting in the formation of a felt-like preform ormaterial thickness on the mold surface. The mold head 4, 14 is thenremoved from the suspension, and the remaining water/suspension mediumis pulled from the blank via the vacuum to thereby produce a preform ofa preset dryness. During the molding operation, the orientation of themold head 4, 14 may or may not be changed in relative three dimensionswithin tank 1, which could lead to different material properties (e.g.thickness), among other things.

The suspension formulation used to achieve the desired product is chosenso as to get the desired suspension chemistry and rheology needed toachieve a substantially uniform distribution of the fibers both insuspension and upon precipitation thereof in such a manner so as toproduce an acceptable preform in a timely fashion. Such factors as fibermaterial, sizing, and sizing distribution; base suspension compositionand viscosity; mold shape and configuration; and vacuum characteristicscan affect the generation of the product.

Alternatively, the molding system, 10, can be used to create agreen-state near-net shaped product. This green-state product wouldtypically be a ceramic/ceramic, ceramic/glass, metal/ceramic, orpowdered metal or ceramic, advantageously held together by a temporarybinder. As a green-state product, the product generally has enoughstrength to be handled but requires a further thermal processing step inorder to achieve full strength and/or other (e.g., thermal, electrical,optical) capabilities. The use of a curing oven may be useful inimproving the intermediate strength of the green-state product if aheat-curable resin is used as a temporary binder material in theproduct. In any event, the completed part, if it is a green-statenear-net shaped product upon completion, will then need to befired/sintered to produce the final usable product.

Multi-layer products can be produced using the present invention tothereby achieve the desired characteristics. In such layers, theorientation of layers and mold and part formed, composition, and/orparticle/fiber size distribution, by way of example only, can be variedfor each of the layers. With reference to FIG. 5, multi-layer device,generally represented at 100, is illustrated schematically. Themulti-layer device may comprise a transporter, 101, in the form of aconveyor, gantry or the like illustrated as a loop for convenience. Thetransporter may have associated therewith at least one transport arm,102, wherein each transport arm comprises a mold head, 103. Thetransport arm, 102, sequentially lowers the mold head, 103, into atleast one of a series of tanks, 104, three of which are shown forconvenience without limit thereto. The mold head is moved within thetank as described elsewhere and the pressure is reduced through vacuumports, 104, herein until a first product layer, 105, is formed thereon.Similarly, a second product layer, 106, and third product layer, 107 areformed and the mold head is removed with a multi-layer precursor, 108,adhered thereto. The multi-layer product may be further processes, suchas by drying, and removed from the mold head to form a multi-layeredproduct, 109. The mold head may then be reused. The transport arm, 102,would allow the movement of the mold head into and within the tank andprovide a vacuum to the mold head as would be realized from thedisclosure herein. While illustrated as a continuous process withmultiple tanks and multiple transport arms, the invention can bedemonstrated and is contemplated to be accomplished with a single tankwhich is emptied and recharged. The product layers may be the same ordifferent.

A process for forming a preform is illustrated with reference to FIG. 6.In FIG. 6, mold head, 100, with a vacuum port, 101, is moved through aslurry in the direction of the arrows, 110. At the first position,illustrated at A, the fiber buildup is higher at the leading edge, 102,than at the trailing edge, 103. At position B the mold head is invertedwhich alters the deposition rate of fibers. At position C the previouslydeposited material alters the apparent vacuum at the surface therebyaltering the deposition of fibers. By altering the movement, and vacuumlevel the characteristics of the preform can be altered to accommodatethe necessity for the product. Also, by continually moving the mold headthe fibers can be intertwined to provide a preform of increased strengthrelative to prior art techniques.

While not restricted to any theory, the proposed mechanism of theinvention will be described with reference to FIGS. 7 and 8. FIG. 7illustrates a static deposition of fibers wherein the mold head, 200,comprises a vacuum port, 201 through which a reduced pressure reductionis applied. The mold head may also comprise a vortex generator or fencerepresented schematically at 203 to expand or intensify the formation ofthe vortex. The fibers, 202, align in tangential relationship to thevortex, as illustrated, and deposit in that manner. As realized throughdiligent research this forms a preform with limited strength. FIG. 8illustrates schematically the impact of movement of the mold head. Asthe mold head moves, illustrated by the arrow, the vortex is realignedthereby causing the fibers to become dispersed and to be deposited in anorientation which is no longer aligned. The fibers become randomlyoriented which increases the number of fibers each fiber is in contactwith similar to a woven pattern. This random orientation greatlyincreases the strength of the preform. If the mold head is moved in amanner which is not perpendicular to the vortex, as illustrated in FIG.6 for example, the vortex is further disrupted and fiber deposition isfurther randomized.

As can be seen from the description, and particularly FIGS. 7 and 8 theprocess includes providing a container for holding a material to bemolded. The mold head is preferably equipped with vortex generators, orfences, to expand or intensify the vortex spin and may be mounted aboveor below the mold screen media. The molding head is placed into thematerial wherein the molding head has passages there through. A reducedpressure is applied to the molding head to draw material through thepassages, vortex generators and/or fences. By combining the generatedvortex's and the three dimensional movement of the mold head as thematerial is drawn onto, or repelled from, the mold screen media used onthe mold head to form a part.

Example 1

A carbon fiber solution comprising 35.4 mm (1 inch) carbon fibersobtained from Toho Tenax Co. was suspended in an aqueous solution at0.08 wt % fiber. The carbon fiber solution was placed in a tank. A355.6×355.6 mm (14″×14″) flat text plaque mold head was lowered into thetank until completely submerged in the carbon fiber solution and rotatedless than 45° about its central axis into the flow stream over a timespan of about 18-30 seconds with a vacuum applied to the mold head. Themold head was removed from the solution, the deposited carbon fiberswere dried and observed. The carbon fiber built up on the trailing edgeof the mold head was about twice as thick as the carbon fiber built upon the leading edge. The fibers were approximately aligned and thedeposit was easily peeled in sheet form.

Example 2

A carbon fiber solution was prepared as in EXAMPLE 1. The mold headdescribed in EXAMPLE 1 was lowered into the tank and completelysubmerged, as in EXAMPLE 1. Unlike EXAMPLE 1 the mold head was rotatedand oscillated until the amount of fiber deposited was approximatelyequal to that of EXAMPLE 1. The mold head was removed from the solution,the deposited carbon fibers were dried and observed. The carbon fiberbuild up was more evenly distributed and more randomly oriented and thefibers were difficult to separate relative to EXAMPLE 1.

While this invention has been described as having a preferred design,the present invention can be further modified within the spirit andscope of this disclosure. This application is therefore intended tocover any variations, uses, or adaptations of the invention using itsgeneral principles. Further, this application is intended to cover suchdepartures from the present disclosure as come within known or customarypractice in the art to which this invention pertains.

1. A molding system comprising: a container for holding material to bemolded; a mold head on which material is be molded; at least one armattached to said mold head and capable of moving said mold head inthree-dimensions within said container.
 2. The molding system of claim 1wherein said material is at least one of a pulp, slurry or suspensionmixture.
 3. The molding system of claim 1 wherein said materialcomprises a fiber.
 4. The molding system of claim 3 wherein said fibercomprises at least one fiber selected from carbon fibers, Kevlar® fiber,fiberglass, ceramic fibers, ceramic fiber precursors.
 5. The moldingsystem of claim 1 further comprising a pressure reduction deviceassociated with said mold head capable of drawing material through saidmold head.
 6. The molding system of claim 5 in which said pressurereduction device includes at least one rotary union, such that vacuumpressure may be applied to said mold head while said mold head is indifferent positions within said container.
 7. The molding system ofclaim 6 in which said pressure reduction device varies the vacuumpressure applied to said mold head during the molding operation.
 8. Themolding system of claim 1 in which said arm comprises includes servosfor moving said mold head.
 9. The molding system of claim 8 in whichsaid arm comprises linear servos for moving said mold head within saidcontainer.
 10. The molding system of claim 1 wherein said material drawnthrough said mold head forms a vortex perpendicular to a portion of saidmold head and said portion of said mold head is movable in a directionwhich is not perpendicular to said vortex.
 11. The molding system ofclaim 1 wherein said mold head further comprises a vortex generator.12-23. (canceled)
 24. A molded part formed by the process of: providinga container for holding a material to be molded; placing a molding headinto said material wherein said molding head comprises passagestherethrough; applying a reduced pressure to said molding head to drawmaterial through said passages; moving said molded part in threedimensions within said material; and forming said molded part on saidmolding head.
 25. The molded part of claim 24 in which said containerholds at least one of a pulp, slurry or suspension mixture.
 26. Themolded part of claim 24 wherein said material comprises a fiber.
 27. Themolded part of claim 26 wherein said fiber comprises at least one fiberselected from carbon fibers, fiberglass, ceramic fibers, ceramic fiberprecursors.
 28. The molded part of claim 27 wherein said depletion ofsaid material comprises depletion of said fiber.
 29. The molded part ofclaim 24 further comprising a pressure reduction device associated withsaid mold head capable of drawing material through said mold head. 30.The molded part of claim 29 in which said pressure reduction deviceincludes at least one rotary union, such that vacuum pressure may beapplied to said mold head while said mold head is in different positionswithin said container.
 31. The molded part of claim 30 in which saidpressure reduction device varies the vacuum pressure applied to saidmold head during the molding operation.
 32. The molded part of claim 24in which said arm comprises includes servos for moving said mold head.33. The molded part of claim 24 in which said arm comprises linearservos for moving said mold head within said container.
 34. The moldedpart of claim 24 wherein said material is drawn through said mold headforming a vortex perpendicular to a portion of said mold head and saidportion of said mold head is moved in a direction which is notperpendicular to said vortex.
 35. (canceled)